Aging effect on the mechanical proprieties

of Al7SiMg alloy

 

Effet de vieillissement sur les propriétés mécaniques

de l’alliage Al7SiMg

 

M. Bournane*

Centre Universitaire des Recherches sur l’Aluminium, Université du Québec à Chicoutimi (Québec) Canada

* Corresponding author: E-mail: mbournan@uqac.ca

Received: 30 August 2009; revised version accepted: 16 October 2009

 

Abstract

     The aging effect at 160 ° C on the mechanical properties and the microstructure of the Al7SiMg alloy prepared by sand and permanent casting was studied. It is found that the as-cast alloy contains dendrites and pores. The homogenization at 540 ° C followed by quenching leads to a globulisation of these dendrites. This causes an increase of yield strength, the tensile strength and hardness. The aging increases the hardening of the material through the formation of Mg2Si precipitates. The grain refinement during permanent casting leads to better mechanical properties of the alloy.

 

Keywords: Aluminum; Silicon; Hardness; Tensile.

 

Résumé 

     L’effet du vieillissement à 160 °C sur les caractéristiques mécaniques et la microstructure de l’alliage Al7SiMg, élaboré par coulée en sable et coulée en coquille métallique, a été étudié.  On constate que l’alliage, à l’état brut de coulée, contient des dendrites ainsi que  des pores. L’homogénéisation à 540 °C après trempe conduit à une globulisation de ces dendrites. Cette dernière entraine une augmentation de la limite élastique, la résistance à la traction et  la dureté. Le vieillissement après trempe accentue le durcissement du matériau grâce à la formation des précipités Mg2Si. L’affinement des grains lors de la coulée en coquille mène à des caractéristiques mécaniques meilleures de l’alliage.

 

Mot-clé: Aluminium; Silicium; Dureté; Traction.