Quasi ternary system H3PO4–Ca(OH)2–H2O: Isotherms 30 and 60 °C

 

Système quasi ternaire H3PO4–Ca(OH)2–H2O:

Isothermes 30 et 60 °C

 

K. Labgairi*, A. Jourani, M. Kaddami

 Equipe Physico-Chimie des Procédés; «Laboratoire physico-chimie des Procédés et des Matériaux »;

Faculté des Sciences et Techniques de Settat - Maroc

* Corresponding author. E-mail: labgairi@yahoo.fr

Received: 05 March 2012; revised version accepted: 30 March 2012

 

Abstract

     The solid-liquid equilibria of the quasi ternary system H3PO4–Ca(OH)2–H2O were studied by using a synthetic method based on conductivity measurements. Tow isotherms are established at 30°C and 60°C. The stable solid phases which appear are Ca10(PO4)6(OH)2, CaHPO4,2H2O, CaHPO4, Ca(H2PO4)2,H2O and Ca(OH)2. These solid phases were characterized by using chemical analysis, Infrared Spectroscopy (IR) and X-ray diffraction.

 

Keywords: Quasi ternary system H3PO4–Ca(OH)2–H2O; Phase equilibria solid–liquid; Calcium phosphate; Hydroxyapatite; Dicalcium phosphate dehydrate; Monocalcium phosphate monohydrate and Anhydrous dicalcium phosphate.

 

Résumé

     Les équilibres solide-liquide du système quasi ternaire H3PO4–Ca(OH)2–H2O ont été étudiés par conductimetrie. Deux isothermes 30 et 60 °C ont été entièrement définies. Les phases solides qui se manifestent dans cet intervalle de température sont : Ca10(PO4)6(OH)2, CaHPO4,2H2O, CaHPO4, Ca(H2PO4)2,H2O et Ca(OH)2. Les différentes phases solides mises en jeu ont été caractérisées par analyse chimique, par absorption IR et par diffraction des rayons X.

 

Mots clés : Système quasi ternaire H3PO4–Ca(OH)2–H2O ; Equilibre entre phases solide-liquide ; phosphates de calcium ; Hydroxyapatite ; Phosphate dicalcique dihydraté ; Phosphate monocalcique monohydraté et Phosphate dicalcique anhydre.

 


 