Comparative study of phosphates glasses isolated

in the ternary systems Bi2O3 - M2O3 - P2O5 (M= Sb and B)

 

Etude comparative des verres de phosphates isolés

dans les systèmes ternaires Bi2O3 - M2O3 - P2O5 (M= Sb et B)

 

M. Belfaquir1,2, T. Guedira1*, M. S. D. Elyoubi1 J.L. Rehspringer2

1 Laboratoire des Matériaux, Electrochimie et Environnement, Université Ibn Tofail, Faculté des Sciences, Kénitra, Maroc

2  IPCMS, DCMI UMR 7504 CNRS / UDS - 23 Rue du Lœss 67037 Strasbourg, France

* Corresponding author. E-mail:guedirat@yahoo.fr

Received: 20 June 2012; revised version accepted: 29 September 2012

 

Abstract

     New glass materials were isolated in systems Bi2O3 - M2O3 - P2O5 (M= Sb and B). An infrared spectroscopy study of these glasses showed that the boron and antimony depolymerize more the network glasses with respect to the bismuth. Electrical conductivity of samples, which have a (0,25-y) Bi2O3 - y M2O3 - 0,75 P2O5 composition and are located on the metaphosphates line, increases with the increase of the amount of oxide M2O3 (M= Sb and B).

 

Keyword : Glasses; Phosphate; Infrared; Density; Conductivity.

 

Résumé 

     De nouveaux matériaux vitreux sont isolés dans les systèmes Bi2O3 - M2O3 - P2O5 (M= Sb et B). L’étude par spectroscopie infrarouge de ces verres montre que le bore et l’antimoine dépolymérisent plus la charpente vitreuse que le bismuth. La conductivité électrique, des échantillons de composition Bi0,5-2yM2y (PO3)1,5 est situés sur la droite des métaphosphates, croit avec l’augmentation du taux de l’oxyde M2O3 (M= Sb et B).

 

Mots clé : Verres ; Phosphate ; Infrarouge ; Densité ; Conductivité.

 