Cyclic voltaMmetry evaluation of Real surface of Li-Co3O4 THIN FILMS PREPARD BY CHEMICAL SPRAY PYROLYSIS

Evaluation par voltampérométrie cyclique de la surface

réelle de couches minces de Li-Co3O4 préparées

par pulvérisation réactive

A. Ait Addi, Y. Berghoute, J. Douch, M. Hamdani*

Laboratoire de Chimie-Physique, Faculté des Sciences, Université Ibn Zohr, Agadir

B.P. 8106, Cité Dakhla, Agadir, Maroc

* Corresponding author. E-mail: mohamed.hamdani@caramail.com

Received: 13 January 2004; revised version accepted: 20 June 2005

Abstract

Thin films of Li-Co3O4 have been prepared on glass at 450°C by spray pyrolysis. Their real surfaces were evaluated using cyclic voltammetry in KOH 1M. The experimental results showed that the roughness factors of the cobalt oxides were significantly improved by Li+ doping. However all the containing lithium oxides (with Li/Co = 3, 7, 10 %) exhibit the same real surface area irrespective of amount of Li+.

Keywords: Thin film; Spray: Real surface area: Roughness factor: Capacity of the oxide: Co3O4: Li-Co3O4.

Résumé 

Des couches minces de Li-Co3O4 sont préparées par pulvérisation réactive sur des supports en verre à 450°C. Leur surface réelle est évaluée par voltampérométrie cyclique dans KOH 1M. Les résultats montrent que la présence de Li+ dans la maille de l’oxyde augmente son facteur de rugosité. Cependant les oxydes lithiés (avec Li/Co = 3, 7, 10%) présentent la même surface réelle indépendamment de leur teneur en Li+.

Mots clés : Couche mince ; Pulvérisation réactive ; Surface réelle ; Facteur de rugosité ; Capacité de l’oxyde ; Co3O; Li-Co3O4.