Effect of SULPHIDES ions on electrochemical behaviour of Cu-40Zn alloy in 3% NaCl medium

Effet des ions sulfure sur le comportement électrochimique de l’alliage Cu-40Zn

dans un milieu NaCl 3%

Z. Mountassir*, Z. Ait chikh, A. Srhiri

Laboratoire d’électrochimie et des études de corrosion, Université Ibn Tofail,

Faculté des Sciences, B.P 133, Kénitra 14000, Maroc

* Corresponding author. E-mail: zmountassir@yahoo.fr

Received: 11 March 2005; revised version accepted: 10 March 2006

Abstract

In this work we are interested to the study of the electrochemical behaviour of Cu-40Zn alloy in 3% NaCl medium with and without sulphides at a concentration of 2ppm of S2- ions. Potentiodynamic polarization curves and electrochemical impedance measurements showed that sulphides accelerate the corrosion of alloy in 3% NaCl. This is interpreted by the presence of Cu2S. This compound prevents the formation of the cuprous oxide film responsible of copper protection.

Keywords: Cu-40Zn Alloy; Sulphides ions; Corrosion; Electrochemical methods.

Résumé 

Dans ce travail nous nous sommes intéressés à l’étude du comportement électrochimique de l’alliage Cu-40Zn, dans une solution NaCl 3% aérée, avec ou sans sulfures à une concentration de 2ppm d’ions S2-.

Cette étude a été menée à l’aide d’un couplage de méthodes électrochimiques stationnaires (courbes I-E) et transitoires (impédance électrochimique).

Les résultats obtenus ont montré que l’addition des ions sulfures favorise la corrosion de l’alliage. Ceci a été interprété par la présence des produits de corrosion Cu2S, formés. Ces derniers bloquent la formation de Cu2O responsable de la protection de cuivre.

Mots clés : Alliage Cu-40Zn ; NaCl 3% ; Ions sulfures ; Corrosion ; Méthodes électrochimiques.