AGEING EFFECT ON RELAXATIONS AND TRANSITIONS IN POLY(VINYLIDENE FLUORIDE)

L’effet de vieillissement sur les relaxations et les transitions dans le poly(Fluorure de vinylidène) (PVDF)

A. Gasmi1*, M. Gouasmia1, D. Bicha1, M. Ghers2

1 Laboratoire de Physique du Solide, Département de Physique, université de Annaba BP12 Algérie

2 Laboratoire d’Etudes des Surfaces et Interfaces de la Matière Solide, Département de Physique,

Université Badji Mokhtar B.P12Annaba Algérie

* Corresponding author.

Received: 30 March 2006; revised version accepted: 26 July 2006

Abstract

Mechanical relaxation and Thermal transitions measurements were carried out on PVDF, using a low frequency inverted torsion pendulum and differential scanning calorimeter (DSC) respectively. A comparative study of spectra and thermograms has been performed.

The mechanical relaxation b , observed near -40°C at 1Hz, is associated at the glass transition of the amorphous phase. An ageing phenomenon is proposed to explain thermal events occurring around 50°C in PVDF. The ageing properties of PVDF have been associated with cooperative molecular movements liberated far below the melting point.

Keywords: Polymers; PVDF; Relaxations; Transitions

 

Résumé

Les mesures de relaxation mécanique et des transitions thermiques sont effectuées sur le PVDF, en utilisant la spectrométrie mécanique à basse fréquence et la calorimétrie différentielle à balayage (DSC) respectivement. Une étude comparative entre les spectres et les thermogrammes a été utilisée.

On note la présence d’une relaxation mécanique b autour de –40°C à 1Hz, qui est associée à la transition vitreuse dans la phase amorphe. Un vieillissement à la température ambiante est proposé pour expliquer le pic endothermique qui apparaît autour de 60°C. Les propriétés de vieillissement de PVDF ont été associées aux mouvements moléculaires coopératifs libérés bien au dessous du point de fusion.

Mots clés : Polymères; PVDF; Relaxations; Transitions