ELECTRO-CHEMICAL BEHAVIOR OF STAINLESS SEELS 304L AND

316L IN CHLORIDES

Comportement électrochimique

des aciers inoxydables 304L et 316L en milieux chlorurés 

 

F. Karray1*, N. Chaabane2

1 LaMaCoP, Faculté des Sciences, 3018 Sfax, Tunisie

2 Laboratoire de l’Etat solide, Faculté des Sciences, 3018 Sfax, Tunisie 

* Corresponding author.

Received: 31 March 2006; revised version accepted: 11April 2007

Abstract

The stainless steels are among the main materials used in orthopedic surgery. In spite of their rustproof character these alloys are not immunized completely against the corrosion. Indeed, of deteriorations by stings or by cave are observed frequently. The problem of the resistance to the corrosion is not made of it independent of elements of additions. An optimal content in chromium and in molybdenum is necessary to improve features of the passive movie

Keywords : stainless steel 316L; stainless steel 304L; electro-chemical corrosion; polarization; molybdenum; chromium; middle chloruré; piqûration; activité,passivité.

 

Résumé

Les aciers inoxydables sont parmi les principaux matériaux utilisés en chirurgie orthopédique. Malgré leur caractère inoxydable, ces alliages ne sont pas totalement immunisés contre la corrosion. En effet, des dégradations par piqûres ou par caverne sont fréquemment observées. Le problème de la résistance à la corrosion n’est pas en fait indépendant des éléments d’additions. Une teneur optimale en chrome et en molybdène est nécessaire pour améliorer les caractéristiques du film passif