Synthesis and Characterization of Poly(e-caprolactone)

from e-caprolactone and Differents Diacids

 

Synthèse et Caractérisation de Poly(e-caprolactone)

à partir d’e-caprolactone et Différents Diacides

 

L. Belarbi*, N. Boudouaia , A. Mesli

Laboratoire de Chimie Organique Physique et Macromoléculaire, Faculté des Sciences Université Djilalil Liabes,

B.P 89 Cité El Arbi Ben m’hidi  Sidi Bel Abbès Algérie.

* Corresponding author. E-mail: belarbi.lahcen@caramail.com

Received: 06 December 2006; revised version accepted:23 March 2007

 

Abstract

     e-caprolactone (CL) was polymerized under atmosphere of nitrogen at 130°C in the presence of acid succinic (As), acid adipic (AD) and acid sebacic (ASB).  Infra-red , NMR1H and13C, the titration of the final carboxyl groups and molecular weights SEC showed that the polycaprolactones (PCL) obtained have two final groups carboxyl.  The molecular weights increase during polymerization.

 

Keywords: e-caprolactone; ring-opening polymerisation; diacids; polycaprolactones.

 

Résumé 

    La e-caprolactone (CL) a été polymérisée sous atmosphère d’azote à 130°C en présence d’acide succinique (AS), acide adipique (AD) et acide sébacique (ASB) respectivement. L’Infra-Rouge, les RMN1H et 13C, la titration des groupes carboxyles terminaux et les poids moléculaires CES montrent que les polycaprolactones (PCL) obtenus possèdent deux groupes carboxyles terminaux. Leurs poids moléculaires augmentent au cours de polymérisation.

 