Kinetics of the precipitation in AZ91 alloy

through in situ X-ray diffraction

 

Cinétique de la précipitation dans l’alliage AZ91

par la diffraction des rayons X in situ

 

H. Azzeddine1, S. Abdessameud1, A. Sari2, B. Alili1, D. Bradai1*

1 Faculté de Physique, USTHB, BP 32 El-Alia, Bab-Ezzouar, Alger, Algérie

2 Centre Nucléaire de Birine, P.O. Box 180, Ain Oussera, 17200, Algérie

* Corresponding author. E-mail: bradai_djamel@yahoo.fr

Received: 28 January 2008; revised version accepted:08 September 2008

 

Abstract                                                                         

     The macroscopic kinetics of the discontinuous precipitation in an AZ91 alloy at 200°C was determined through in situ Xray Diffraction via the integral intensity and also by Vickers microhardness measurements. It is shown that the macroscopic kinetics can be well described by the Johnson-Mehl-Avrami law and that the n Avrami parameter indicates that the precipitation proceeds by a mechanism of nucleation after site saturation.

 

Keywords: AZ91 alloy; Precipitation; Kinetics; XRD.

 

Résumé

     La cinétique macroscopique de la précipitation discontinue dans l’alliage AZ91 a été déterminée à 200°C au cours d'une expérience de diffraction des rayons X in situ par la mesure de l'intensité intégrée des pics du précipité et par des mesures de microdureté Vickers. La cinétique macroscopique de la précipitation discontinue peut être décrite par la loi de Johnson-Mehl-Avrami. L’exposant n semble indiquer un mécanisme qui opère par germination après saturation des sites.

 

Mots clés: Alliage AZ91;  Précipitation; Cinétique; DRX.