PREPARATION ET CARACTERISATION D’UN CATALYSEUR

A BASE PHOSPHATE DE FER

E. Chemseddine, M. Zoubir, A. El Hajbi*

Laboratoire de Chimie Physique, Faculté des Sciences, Université Chouaib Doukkali, B.P. 20, 2400 EL Jadida, Maroc

* Corresponding author. E-mail : el_hajbi@ucd.ac.ma

Received : 10 January 2001; revised version accepted 01 October 2001

Abstrat 

CoFePO5 was prepared by dry synthesis from Fe2 O3 , (NH4 )2 HPO4 and CoCO3 , or from FePO4 and CoCO3 . the X-ray diffractogram at room temperature was indexed in the orthorhombic system (space group Pnma) by isotyping with a FePO5. The parameters of the crystal lattice were influenced by the substitution of Fe2+ for Co2+. IR spectroscopy showed vibration of the P-O band of the PO4 tetraedra. The E.P.R spectrum at low temperature (4K) showed two values of g corresponding to Fe2+ and Co2+ in the octahedral sites

Keywords: Oxyphosphate ; Catalyst ; X-ray ;IR ; EPR.

Résumé 

Le composé CoFePO5 est obtenu à partir de Fe2 O3 , (NH4)2HPO4 et CoCO3 , ou à partir de FePO4 et CoCO3 , par voie sèche à 900° C. Son diffractogramme des rayon X est indexable à température ambiante dans le système orthorhombique (groupe d’espace Pnma) par isotope avec a Fe2 PO5 . Les paramètres de la maille cristalline sont influencés par la substitution de Fe2 + par Co2 +. La spectroscopie IR a montré des vibrations de la liaison P-O des tétraèdres PO4 . Le spectre R.P.E à basse température (4k) montre deux valeurs de g qui correspondent à Fe2 + et Co2 + dans des sites octaédriques.

Mots clés: Oxyphosphate ; Catalyseur ; Rayon X ; IR ; R.P.E.