UN NOUVEAU POLYMERE CONJUGUE

POUR LA REALISATION DES DIODES ELECTROLUMINESCENTES

M. Bouachrine1*, J. P. Lère-Porte2, J. Moreau2, F. Serein Spirau2, R. Augusta Silva2,

K. Lmimouni3 , C. Dufour3

1LRMM, Faculté des Sciences et Techniques d’Errachidia, B.P. 509 Boutalamine Errachidia, Maroc

2 Hétérochimie Moléculaire et Macromoléculaire, UMR CNRS 5076,

E.N.S.C.M, 8 rue de l’Ecole Normale, 34296 Montpellier Cedex 05, France

3IEMN DHS - UMR CNRS 8520 - Université des Sciences et Technologies de Lille

Avenue Poincaré, B.P. 69, 59652 Villeneuve d'Ascq Cedex, France

* Corresponding author. E-mail: mbouach@hotmail.com

Received : 23 October 2001; revised version accepted :14 February 2002

Abstract

A dialkoxyphenylene-thienylene copolymer was prepared by using an organometallic condensation reaction. The grafting of polar side chains gave to the polymer a good solubility in most organic solvents and excellent adhesion properties on glass. It allowed the formation of homogenous thin films on ITO by spin coating. A single layer light emitting diode was fabricated in the configuration of ITO (Indium Tin Oxide)/polymer/Al. Electroluminescent maximum was recorded at 600 nm corresponding to a red-orange emission. The diode exhibited an operating voltage at c.a. 5V and a high current rectification ratio (3x103).

Keywords: Conducting polymers; Electroluminescence; LED.

Résumé

Un copolymère dialkoxyphenylène thiophène a été préparé en utilisant une réaction de couplage organométallique. Le greffage sur le squelette conjugué, des chaînes polaires confère à ce matériau une bonne solubilité dans des solvants organiques et d'excellentes propriétés d’adhésion sur verre. Une diode électroluminescente émettant dans le rouge-orangé avec une tension de 5V a pu être élaborée.

Mots clés : Electroluminescence; LED; Polymère conjugué; Copolymère.