COMPORTEMENT D’ACIER INOXYDABLE AUSTENITIQUE 316

AUX SOLLICITATIONS MECANIQUES

CAUSEES PAR INDENTATION APRES UN TRAITEMENT CHIMIQUE

L. Farah1*, A. Azzi2

1 Faculté des Sciences et Techniques Mohammadia

Quartier Yassmina Route de Rabat B.P 146 Mohammadia, Morocco

2 Faculté des Sciences Ain Chok Route d’Eljadida Casablanca, Morocco

* Corresponding author. E-mail : lahbibfarah@yahoo.com ou Farah@uh2m.ac.ma

Received : 17 February 2002; revised version accepted : 18 July 2002

Abstract

In our study, conducted with dynamic indentation tests on an AISI stainless steel, in elastoplastic conditions, we have proved that the hardness variations at the bottom of the contact area induced by the ball impacts on the sample surface are conneted to the initial surface etat. More over, in our tests conditions, we have pointed out that this hardness and the contact area radius reach a stable value after 1000 cycles. This is due to an adaptation of the material.

Keywords: Stainless steel ; Dynamic indentation; Hardness; Pitting.

Résumé

Dans l’étude que nous avons conduite en indentation dynamique en régime élastoplastique sur un acier inoxydable austénitique de type 316, nous avons montré que les variations de dureté en fond d’empreinte occasionnées par la répétition des chocs d’une bille sur la surface de l’échantillon sont corrélées à l’état de surface initiale. De plus nous avons constaté que cette dureté ainsi que le diamètre de l’empreinte arrivent au bout de 1000 cycles dans nos conditions d’essai à des valeurs stables correspondant à une accommodation du matériau.

Mot clés : Acier inoxydable ; Indentation dynamique ; Dureté ; Piqûration.