ETUDE ELECTROCHIMIQUE DE L'INFLUENCE DU LAMINAGE

SUR LA RESISTANCE A LA CORROSION

DE L'ALLIAGE D'ALUMINIUM 3003 EN MILIEU NaCl 3%

A. Tahani1*, E. Chaieb1, S. Kertit2, A. Chacrone3, M. Benkaddour1

1 Laboratoire d'Analyse et de caractérisation des matériaux. Faculté des sciences d'Oujda, Maroc
2 Laboratoire de physico-chimie des matériaux, Ecole Normale Supérieure de Takaddoum,

BP. 5118, Rabat, Maroc.
3 Lamat . E.S.S.E.T.Rabat. B.P. 6207, Rabat Institut, Rabat Maroc

* Corresponding author. E-mail :sanaamerimi@iam.net.ma

Received : 29 January 2002; revised version accepted : 26 November 2002

Abstract

Electrochemical Behaviour of Aluminium 3003 Alloy have been tested in 3% NaCl with and without rolling. For this experience, two rolling percentages have been chosen (70% and 90%). The obtained results showed that the 90% percentage rolling was the best. Polarisation measurements show that the texture caused by the rolling at 90%, presents the best resistance to corrosion.

Keywords: Corrosion; Rolling; Aluminium; 3% NaCl; Texture.

Résumé

L'étude du comportement électrochimique d'un alliage d'aluminium 3003 a été étudié dans une solution de chlorure de sodium en l'absence et en présence de laminage. Deux pourcentages de laminage (70% et 90%) ont été choisis pour cette étude. Les résultats obtenus montrent que la texture provoquée par le laminage à 90%, présente la meilleure résistance à la corrosion.

Mots clés: Corrosion ; Laminage ; Aluminium ; Nacl 3% ; Texture.