SYNTHESE DE ZEOLITHE DE TYPE MFI

A PARTIR DE SOLUTIONS AQUEUSES DE FLUOROSILICATES

EN PRESENCE DE MOLECULES GENERATRICES DES IONS OH-

A . El Alaoui*

L.R.M.M, Département de chimie, Faculté des Sciences et Techniques,

Université Moulay Ismaïl, B.P. 509 Boutalamine Errachidia, Morocco

* Corresponding author. E-mail : aelalaoui1@caramail.com

Received : 30 January 2002; revised version accepted : 15 September 2002

Abstract

MFI-type zeolite is crystallized from aqueous solutions through the hydrolysis of soluble fluorosilicates. The required pH increase resulting from the thermal decomposition of urea or cyanamide. Depending on the chemical composition and the physical parameters, the crystallization takes place most often through the intermediate formation of a gel, although under special conditions, it may proceed directly from the solution. Crystal sizes up to 1000 µm were obtained. Chemical analysis and NMR spectroscopy of these products show no significant differences with products prepared conventionally from gels.

Keywords: Zolite; Thermal decomposition; Urea; Cyanamide.

Résumé

La cristallisation de la zéolithe de type MFI à partir de solutions aqueuses stables de fluorosilicates, a lieu grâce à la présence dans le milieu d’urée ou de cyanamide permettant l’augmentation de pH par suite d’une décomposition hydrothermale in situ. La cristallisation de la zéolithe dépends des paramètres physiques et chimiques et passe souvent par l’étape de formation du gel. Cependant dans certaines conditions, il semble que la cristallisation a lieu directement à partir de solution, des cristaux d’une taille de1000 µm ont été obtenus . L’analyse chimique et spectroscopique des cristaux synthétisés ne montre pas de différence significative avec les produits obtenus à partir du gel.

Mots clés : Zéolithe ; Décomposition hydrothermale ; Urée ; Cyanamide.