INFRARED SPECTROSCOPIC STUDIES

OF TERNARY CoO-MoO3-P2O5 GLASSES

Etude par spectroscopie Infrarouge

des verres du systeme ternaire CoO-MoO3-P2O5

N. Mouhsine, N. Allali, L. Bih, A. Yacoubi, A. Nadiri*

UFR Sciences des Matériaux Inorganiques, Département de Chimie, Faculté des Sciences,

B.P. 4010 Beni M'hamed, Meknès, Maroc

* Corresponding author . E-mail : a.nadiri@fsmek.ac.ma

Received : 26 November 2002; revised version accepted : 02 August 2004

Abstract

The structure of glass belonging to the ternary system CoO-MoO3-P2O5 has been studied by infrared spectroscopy. The investigation has been carried out on three series of glasses : xCoO-(0.50-x)MoO3 - 0.50P2O5 (series 1) ; xCoO-(0.67-x)MoO3-0.33P2O5 (series 2) and x CoO-(0.75 - x) MoO3-0.25P2O5 (series 3) with x = 0 ; 0.05 ; 0.1 ; 0.15 ; 0.20 and 0.25. Vibrational spectroscopy has evidenced vibrational modes related to PO2- ; PO32-, PO43-, MoO4 and MoO6 groups.

Keywords: Glasses; Phosphate; Molybdenum; Cobalt; Infrared spectroscopy.

Résumé

La structure des verres issus du système ternaire CoO-MoO3-P2O5 a été étudiée par spectroscopie infrarouge pour trois séries de verres de composition : x CoO - (0,50 - x) MoO3 - 0,50 P2O5 (série 1) ; x CoO - (0,67 - x) MoO3 - 0,33 P2O5 (série 2) et x CoO - (0,75 - x) MoO3 -0,25 P2O5 (série 3) avec x = 0 ; 0,05 ; 0,1 ; 0,15 ; 0,2 et 0,25. Le réseau vitreux est formé de groupements phosphate et molybdate à savoir PO2- ; PO32-, PO43-, MoO4 et MoO6.

Mots clés : Verre ; Phosphate ; Molybdène ; Cobalt ; Spectroscopie infrarouge.