Dielectric anomalies at high temperature

in sol gel processed BZT ceramics

 

Anomalie diélectriques à haute température

dans les céramiques BZT préparées par voie sol-gel

 

A. Ameziane El Hassani1, T. Lamcharfi1,2, S. Sayouri1*, N.S. Echatoui1,2, D. Mezzane3, L.Hajji3

1 LPTA, Département de Physique, Faculté des Sciences DM, BP 1796, Fès Morocco

2 LSSC, Département de Génie électrique,Faculté des Sciences et Techniques, Fès Morocco

3 LESPO, Département de Physique, FST Guéliz Marrakech Morocco

* Corresponding author. E-mail: ssayouri@yahoo.com

Received : 02 March 2007; revised version accepted:24 July 2007

 

Abstract

     Sol-gel processed Ba(Zrx, Ti1-x)O3, x = 0; 0.1; 0.2 and 0.5, ceramic powders have been characterized by X ray diffraction (XRD) and by dielectric measurements. Interesting dielectric characteristics are revealed by the existence of anomalies in both the ferroelectric phase (FP) and the paraelectric one (PP). The grain size, the method of elaboration and oxygen vacancies may explain the origin of these anomalies.

 

Keywords:  BaTiO3; Dielectric anomalies; Hydrothermal method.

 

Résumé

     Des poudres Ba(Zrx Ti1-x)O3, x = 0, 0.1, 0.2 et 0.5 ont été préparées par voie sol gel et caractérisées aux rayons X et par des mesures diélectriques. Ces dernières présentent des caractéristiques intéressantes quant à l’existence d’anomalies, aussi bien dans la phase ferroélectrique (FP) que dans la phase paraélectrique (PE). La taille des grains, la méthode de préparation des poudres ainsi que les sites vacants en oxygène peuvent expliquer l’origine de ces anomalies.

 

Mots clés : BaTiO3 ; Anomalies diélectriques ; Méthode hydrothermale